铜

  铜
UNS C10200 C11000 C14530 C15100 C15500 C19400 C19500 C19700
  OFHC
99.95 Cu		 ETP
99.90 Cu		 99.9 Cu .02 Te .02 Sn ZHC
99.9 Cu .1 Zr		 99.80 Cu .04 Ag
.05 P .11 Mg		 97.5 Cu 2.35 Fe
.03 P .12 Zn		 97 Cu 1.5 Fe .1 P
.8 Co .6 Zn		 99.8 Cu
.25 P .70 Fe .10 Mg
密度 (1) .323 .321 .323 .323 .322 .322 .322 .321
弹性系数 (2) 17 17 17.4 17 17 17.5 17.3 17
导电率 (3) 101 100 96 95 86 60 50 80
导热率 (4) 226 224 224 208 200 150 115 185
热膨胀系数 (5) 9.8 9.8 9.8 9.9 9.9 9.0 9.4 9.6
成本因子 (6) 1.08 1.00 0.99 1.01 .99 .99 1.05 .95
退火
UTS (7)
YS (8)
EL (9)
HV (10)		 C10200
26-38
6-13
20-42
52 nom.		 C11000
26-38
6-13
20-42
52 nom.		 C14530
---
---
---
---		 C15100
33-43
10-20
30-40
55 nom.		 C15500
34-43
15-22
30-42
75 nom.		 C19400
40-50
20-40
15-35
80 nom.		 C19500
50-60
21-35
22-31
---		 C19700
45-53
---
20 min
---
1/4 Hard
UTS
YS
EL
HV		 C10200
34-42
26-39
13-33
70-95		 C11000
34-42
26-39
13-33
70-95		 C14530
35-45
26-37
23
85-105		 C15100
40-45
34-46
12-25
90 nom.		 C15500
42-50
33-40
20-28
105 nom.		 C19400
45-60
40-56
6-20
95-120		 C19500
60-72
45-79
5-23
112-145		 C19700
---
---
---
---
1/2 Hard
UTS
YS
EL
HV		 C10200
37-46
30-44
8-32
88-105		 C11000
37-46
30-44
8-32
88-105		 C14530
41-49
38-48
12
95-115		 C15100
43-51
40-52
14-13
105 nom.		 C15500
45-55
38-48
13-22
113 nom.		 C19400
53-63
45-58
4-15
100-125		 C19500
68-78
66-76
3-9
140-155		 C19700
53-63
36-60
6-29
122-144
3/4 Hard
UTS
YS
EL
HV		 C10200
41-50
39-48
5-24
92-110		 C11000
41-50
39-48
5-24
92-110		 C14530
44-52
43-51
6
100-120		 C15100
47-56
46-57
2-7
115 nom.		 C15500
48-58
45-54
7-13
118 nom.		 C19400
---
---
---
---		 C19500
75-85
72-82
2-5
150-160		 C19700
---
---
---
---
Hard
UTS
YS
EL
HV		 C10200
43-52
41-50
3-16
99-116		 C11000
43-52
41-50
3-16
99-116		 C14530
47-54
46-53
3
108-122		 C15100
53-62
50-61
1-5
122 nom.		 C15500
56-64
50-60
6-12
126 nom.		 C19400
60-70
53-65
2-8
120-140		 C19500
82-90
79-87
2-3
55-165		 C19700
60-70
53-68
2-12
132-153
Ex. Hard
UTS
YS
EL
HV		 C10200
47-56
46-55
3-5
103-120		 C11000
47-56
46-55
3-5
103-120		 C14530
50-60
49-59
2.5
110-126		 C15100
59-65
54-64
1-3
129 nom.		 C15500
60-70
56-64
3-7
130 nom.		 C19400
67-73
57-68
1-3
125-145		 C19500
---
---
---
---		 C19700
67-73
64-71
2-10
144-158
Spring
UTS
YS
EL
HV		 C10200
50-58
48-57
2-4
110-126		 C11000
50-58
48-57
2-4
110-126		 C14530
54-64
53-58
2
112-128		 C15100
64-71
59-69
1-2
136 nom.		 C15500
66-75
62-74
1-5
135 nom.		 C19400
70-76
60-71
1-2
130-150		 C19500
88-97
85-92
1-2
165-175		 C19700
70-76
67-74
2-8
148-164
Ex. Spring
UTS
YS
EL
HV		 C10200
52 min
51 min
1-3
115 min.		 C11000
52 min
51 min
1-3
115 min.		 C14530
58 min
57 min
2
115 min		 C15100
---
---
---
---		 C15500
76-86
72-78
1-4
---		 C19400
73-80
63-74
2 max
---		 C19500
97 min
94 min
1-2
180 min		 C19700
73-80
70-78
1 min
153-174

* 注意

(1)磅/立方英寸@60华氏度(退火)
(2)弹性系数在张力 x 106 P.S.I.
(3)%国际退火铜标准导电率@ 68 华氏度
(4)英制热单位/平方英尺/小时/华氏度 @ 68 华氏度
(5)英寸/英寸 x 10-6 从68华氏度到572华氏度
(6)大约的相对成本: 基于电解韧铜带材1.00; 0.025英寸x 1.00英寸 10 米 磅. 数量
(7)拉伸极限强度x1000 P.S.I.
(8)0.2%残余变形屈服强度x 1000 P.S.I. 因为它们的有效性, 黄铜厂不使用或接受屈服强度为规格标准, 此处给的值仅为设计目的需要。
(9)% 伸长率 @ 2". 伸长率值因厚度而有很大的不同。给出的轧制韧度数据是基于厚度从 0.010英寸 到0.035英寸的带材。
(10)大约的维氏硬度 - Hv (除非另外指定)

注意: 这些表格提供的特征仅供参考