  Aluminum Glass Sealing
UNS A91100 A93003 A95052 K94610 K94100
  1100 Aluminum
99.0 min Al .12 Cu		 3003 Aluminum
1.2 Mn .12 Cu Bal Al		 5052 Aluminum
2.5 Mg .25 Cr Bal Al		 Kovar
29 Ni 17 Co Bal Fe		 A-42
42 Ni .02 C .15 Si .80 Mn Bal Fe
Density (1) .098 .099 .097 .302 .293
Mod.of Elast. (2) 10.0 10.2 10.1 20 21.5
Elect.Cond. (3) 59 50 35 3.5 2.4
Thermal Cond. (4) 128 112 79 120 74.5
Coefficient of
Therm Expan. (5)		 14.1 13.9 14.3 2.85 2.71
Cost Factor (6) .83 .85 .85 7.91 2.78
Annealed
UTS (7)
YS (8)
EL (9)
HV (10)		 A91100
13 nom
5 nom
35 nom
HB23 nom		 A93003
16 nom
6 nom
30 nom
HB28 nom		 A95052
28 nom
13 nom
25 nom
HB36 nom		 K94610
70-90
35-75
18-32
130-200		 K94100
70-90
35-75
18-32
130-200
1/4 Hard
UTS
YS
EL
HV		 A91100
---
---
---
---		 A93003
---
---
---
---		 A95052
---
---
---
---		 K94610
85-100
75-93
10-19
190-250		 K94100
85-100
75-93
10-19
190-250
1/2 Hard (H12)
UTS
YS
EL
HV		 A91100
16 nom
15 nom
12 nom
HB28 nom		 A93003
19 nom
18 nom
10 nom
HB35 nom		 A95052
33 nom
28 nom
9 nom
HB46 nom		 K94610
93-108
89-104
7-12
230-260		 K94100
93-108
89-104
6-12
230-260
3/4 Hard
UTS
YS
EL
HV		 A91100
---
---
---
---		 A93003
---
---
---
---		 A95052
---
---
---
---		 K94610
98-113
95-110
5-8
240 min		 K94100
98-113
95-110
4-8
240 min
Hard (H14)
UTS
YS
EL
HV		 A91100
18 nom
17 nom
9 nom
HB32 nom		 A93003
22 nom
21 nom
8 nom
HB40 nom		 A95052
38 nom
31 nom
8 nom
HB53 nom		 K94610
102-117
99-115
3-5
250 min		 K94100
102-117
99-115
3-6
250 min
Ex. Hard
UTS
YS
EL
HV		 A91100
---
---
---
---		 A93003
---
---
---
---		 A95052
---
---
---
---		 K94610
107-125
105-122
2-4
---		 K94610
107-125
105-122
2-4
---
Spring (H16)
UTS
YS
EL
HV		 A91100
21 nom
20 nom
6 nom
HB38 nom		 A93003
26 nom
25 nom
5 nom
HB47 nom		 A95052
40 nom
35 nom
7 nom
HB58 nom		 K94610
---
---
---
---		 K94100
---
---
---
---
Ex. Spring (H18)
UTS
YS
EL
HV		 A91100
24 nom
22 nom
5 nom
HB44 nom		 A93003
29 nom
27 nom
4 nom
HB55 nom		 A95052
42 nom
37 nom
6 nom
HB63 nom		 K94610
---
---
---
---		 K94100
---
---
---
---

NOTES

(1)Lbs.per cubic inch @ 60°F (annealed)
(2)Elastic modulus in tension x 106 P.S.I.
(3)% IACS at 68°F
(4)BTU per sq. ft. per hour per °F at 68°F
(5)Inches per inch x 10-6 from 68°F to 572°F
(6)Approximate relative cost based on ETP copper as 1.00; .025" x 1.00" strip in 10 m lbs. quantity
(7)Ultimate tensile strength x1000 P.S.I.
(8)0.2% offset yield strength x 1000 P.S.I. Yield strengths are not used or accepted as specifications by brass mills; but, because of their usefulness, values are given here for design purposes
(9)% elongation in 2". Elongation values vary considerably with thickness. The rolled temper data given are based on thicknesses ranging from .010" to .035" strip.
(10)Approximate Vickers hardness - Hv unless otherwise specified.

NOTE: The properties on these charts are provided for reference only.