Reroll Capabilities and Alloys / Copper




Most non-proprietary alloys available.

Most tempers available

Gauges from .005" - .010" x 6.000"
maximum width and .0025" - .005" x
3.500" maximum width.

Heavier gauges and wider widths are
dependent upon material availability.

Minimum buy is generally 100 lbs.








If you are looking for
something outside
the parameters listed,
please give us a call!

We may have a solution!












Request a Quote

C10200

OFHC copper

99.95 Cu
10 ppm
0 max		 C10700*

OFS
copper

99.9Cu
.085 min.
Ag

C11000

ETP
copper

99.9Cu

 C12200

DHP
copper

99.9Cu
.025P		 C15100

ZHC
copper

99.8Cu
.15Zr		 C15500




99.75Cu
.11Mg
.06Ag
.06P		 C18080


K88

99Cu
.5Cr .2Ag
.1Fe .1Ti
.05Si
Density(1)
Modulus(2)
Elect.Cond.(3)
Therm.Cond.(4)
Therm. Exp.(5)
ASTM(6)		 .323
17
101
226
9.8
B152		 .323
17
100
224
9.4
B152		 .322
17
100
224
9.8
B152		 .323
17
85
196
9.8
B152		 .323
17.5
95
208
9.8
B888		 .322
17
86
200
9.8
B888		 .320
19.5
80
185
9.8
Annealed
UTS(7)
YS(8)
EL(9)
HV(10)
26-38
6-13
20-42
40-75
26-38
6-13
20-42
40-75
26-38
6-13
20-42
40-75
26-38
6-13
20-42
40-75
37-42
9-20
35 nom.
55 nom.
34-43
15-22
30-42
65 nom.
1/4 Hard
UTS
YS
EL
HV
34-42
26-39
13-33
70-95
34-42
26-39
13-33
70-95
34-42
26-39
13-33
70-95
34-42
26-39
13-33
70-95
40-45
26-40
11-25
90 nom.
42-50
33-40
20-28
95 nom.
1/2 Hard
UTS
YS
EL
HV
37-46
30-44
8-32
85-105
37-46
30-44
8-32
85-105
37-46
30-44
8-32
85-105
37-46
30-44
8-32
85-105
43-51
35-48
3-13
105 nom.
45-55
38-48
13-22
113 nom.
3/4 Hard
UTS
YS
EL
HV
41-50
39-48
5-24
90-110
41-50
39-48
5-24
90-110
41-50
39-48
5-24
90-110
41-50
39-48
5-24
90-110
47-56
45-55
1-7
115 nom.
48-58
45-54
7-13
118 nom.
Hard
UTS
YS
EL
HV
43-52
41-50
3-16
95-115
43-52
41-50
3-16
95-115
43-52
41-50
3-16
95-115
43-52
41-50
3-16
95-115
53-62
51-61
1-5
122 nom.
56-64
50-60
6-12
126 nom.		 TM04
71-81
65 min.
8 nom.
140-170
Extra Hard UTS
YS
EL
HV
47-56
46-55
3-5
103-120
47-56
46-55
3-5
103-120
47-56
46-55
3-5
103-120
47-56
46-55
3-5
103-120
59-65
57-64
1-3
129 nom.
63-72
58-64
3-7
130 nom.		 TM08
77-87
85 min.
4 nom.
150-180
Spring
UTS
YS
EL
HV
50-58
48-57
2-4
110-126
50-58
48-5
2-4
110-126
50-58
48-57
2-4
110-126
50-58
48-57
2-4
110-126
64-71
62-70
1-2
126 nom.
65-73
60-74
1-5
135 nom.		 TR08
75-90
72 min.
4 nom.
160-190
Ex. Spring UTS
YS
EL
HV
52 min.
51 min.
1-3
115 min.
52 min.
51 min.
1-3
115 min.
52 min.
51 min.
1-3
115 min.
52 min.
51 min.
1-3
115 min.

68-75
63-78
1-4









*Dependent upon material availability.
CHART FOOTNOTES
1 Lbs. per cubic inch @ 68°F (annealed)
2 Elastic modulus in tension x 106 P.S.I.
3.% IACS at 68°F (annealed)
4. BTU per foot per hour per °F at 68°F (annealed)
5. Inches ber inch x 10-6 from 68°F to 572°F
6. Reference specification for strip
7. Ultimate tensile strength x 1000 P.S.I.
8. 0.2% offset yield strength x 1000 P.S.I. Yield strengths are not used or accepted as specifications by brass mills; but because of their usefulness, values are given here for design purpose.
9. % elongation in 2". Elongation values vary considerably with thickness. The rolled temper data given are base on thicknesses ranging from .010" to .035" strip.
10. Approximate Vickers hardness - HV unless otherwise specified.
11. Standard heat treatment 2 hrs. at 600°F (3 hrs. @ 600°F for annealed temper)
12. Standard heat treatment 2 hrs. at 700°F (2 hrs. @ 675°F for TS04)