C70250
96.2Cu
3 Ni
.6 Si
.2 Mg |
C70260
97.5 Cu
2 Ni
.5 Si |
C70600
Cupro
Nickel
88.6 Cu
10 Ni
1.4 Fe |
C71500
Cupro
Nickel
69.4 Cu
30 Ni
.6 Fe |
C72500
88.2Cu
9.5 Ni
2.3 Sn |
C72900
as
rolled
77 Cu
15 Ni
8 Sn |
C72900
age
hard(12)
77 Cu
15 Ni
8 Sn |
C72900
mill
hard
77 Cu
15 Ni
8 Sn |
C73500
Nickel
Silver
72 Cu
10 Zn
18 Ni |
C75200
Nickel
Silver
65 Cu
17 Zn
18 Ni |
C76200*
Nickel
Silver
59 Cu
29 Zn
12 Ni |
C77000
Nickel
Silver
55 Cu
27 Zn
18 Ni |
Density(1)
Modulus(2)
Elect. Cond.(3)
Therm. Cond.(4)
Therm. Exp.(5)
ASTM(6) |
.318
19
40
85
10.0
B422 |
.320
19
40
90
B422 |
.323
20
9.1
23
9.5
B122 |
.323
22
4.6
17
9.0
B122 |
.321
20
11
31
9.2
B122 |
.321
18.5
7.8
17
9.1
B740 |
.321
18.5
7.8
17
9.1
B740 |
.321
19.5
7.8
17
9.1
B740 |
.319
18.000
8.000
21.500
9.000
B122 |
.316
18
6
19
9.0
B122 |
.310
18
9
24
8.5
B122 |
.314
18
5.5
17
9.3
B122 |
Annealed
UTS(7)
YS(8)
EL(9)
HV(10) |
TM00
90-110
65-90
10 min. |
TM00
85-95
75 min.
15 min.
190 nom. |
65-90 |
50-65
20-40
25 Min.
80-110 |
45-65
18-25
34-36
80-110 |
TB00
64-85
24-40
32 Min.
100-150 |
TX00
120-150
100-130
6 Min.
275-350 |
TM00
95-115
75-95
22 Min.
190-290 |
50-68
15-60
11-37
89-145 |
53-63
18-32
29-42
78-120 |
57-75
21-52
32-49
92-145 |
61-76
23-41
39-48
83-135 |
1/4 Hard
UTS
YS
EL
HV |
|
|
51-67
95-146 |
58-72
35-69
5-30
120-155 |
55-75
73 Max.
5 min.
164 Max |
TD01
75-100
50-75
18 Min.
150-235 |
TS01
130-160
115-145
4 Min.
290-365 |
|
56-69
28-59
10-25
119-151 |
58-72
26-64
14-35
95-138 |
65-81
36-68
20-50
110-167 |
69-87
44-83
11-41
126-179 |
1/2 Hard
UTS
YS
EL
HV |
TM02
95-120
85-119
7 min. |
TM02
95-105
95 min.
6 min.
210 nom. |
|
66-80
60-78
3-10
140-170 |
65-80
59-78
3-17
132-180 |
TD02
85-110
65-100
8 Min.
170-275 |
T202
145-175
135-165
3 Min.
315-390 |
TM02
105-125
90-110
15 Min.
215-315 |
63-75
49-69
3-16
138-164 |
66-80
48-78
6-22
122-157 |
75-91
58-82
6-30
145-193 |
78-95
64-93
5-24
154-198 |
3/4 Hard
UTS
YS
EL
HV |
TM03
100-125
95-120
5 min. |
|
|
|
|
95-120
90-115
3 Min.
210-290 |
TS03
155-185
145-175
2 Min.
325-400 |
|
69-79
59-73
2-5
142-171 |
74-86
69-82
4-12
138-175 |
83-98
73-91
4-16
160-203 |
88-101
84-100
3-13
171-193 |
Hard
UTS
YS
EL
HV |
|
|
71-83
140-174 |
75-88
73-84
2-4
160-185 |
75-90
73-88
1-5
135-180 |
TD04
100-130
85-125
1 min.
220-300 |
T204
165-195
155-185
2 min.
335-410 |
TM04
115-135
105-125
10 min.
245-345 |
73-84
67-78
1-3
160-180 |
78-91
75-90
3-7
151-188 |
90-105
82-97
3-6
188-215 |
92-109
90-108
3-6
188-220 |
Extra Hard
UTS
YS
EL
HV |
|
|
73-85
158-192 |
80-92
78-88
1-3
165-195 |
80-95
78-93
1-3
153-218 |
|
|
TM06
130-150
120-145
6 min.
270-370 |
79-90
72-81
1-2
170-190 |
86-98
85-97
3-4
175-209 |
99-114
93-103
1-3
209-234 |
102-115
101-114
1-2
214-240 |
Spring
UTS
YS
EL
HV |
|
|
78-86
164-196 |
84-94
81-90
1-2
174-200 |
85-100
83-97
1-2
164-218 |
TD08
122-145
100-140 |
|
TM08
150-178
140-170
2 min.
305-405 |
85-93
78-84
1
180-200 |
90-101
88-99
1-2
183-220 |
107-122
101-110
1-2
228-250 |
108-123
107-118
1
228-250 |
Ex. Spring
UTS
YS
EL
HV |
|
|
|
|
90-105
88-102
1
187-218 |
|
|
|
88 Min.
78 Min.
1
185 Min. |
96 Min.
95 Min.
1-2
198 Min. |
114 Min.
102 Min.
1
235 Min. |
116 Min.
115 Min.
1
235 Min. |
|
|
|
|
|
|
|
|
|
|
|
|
|