Reroll Capabilities and Alloys / Refractory Metals
 |
If you are looking for
something outside
the parameters listed,
please give us a call!
We may have a solution!
|
|
R04200
Reactor
Grade
Niobium
Nb |
R05200
Unalloyed
Tantalum
Ta |
R50250
Grade 1
Titanium
Ti |
R60702
Unalloyed
Zirconium
99.2 Zr |
Density (1)
Modulus (2)
Elect. Cond. (3)
Therm. Cond. (4)
Therm. Exp. (5)
ASTM (6) |
.310
15
11.5
30
4.1
B393 |
.600
27
14
34
3.7
B70 |
.163
15
3
9.2
5.1
B26 |
.234
14
4.1
9
3.5
B551 |
Annealed
UTS (7)
YS (8)
EL (9)
HV (10) |
18-38
10-30
20 Min.
55-95 |
30-45
20-40
20 Min.
90-120 |
35-60
25-45
24 Min.
120 Nom. |
55-80
30-65
16 Min.
150 Nom. |
1/4 Hard
UTS
YS
EL
HV |
CW10%
48
43
25
90 |
CW10%
40
35
120 |
CW10%
70
160 |
|
1/2 Hard
UTS
YS
EL
HV |
CW25%
55
53
7
115 |
CW25%
45
42
125 |
CW25%
80
180 |
CW25%
64
18 |
3/4 Hard
UTS
YS
EL
HV |
CW50%
63
62
2
135 |
CW50%
55
53
130 |
CW50%
100
210 |
CW50%
71
15 |
Hard
UTS
YS
EL
HV |
CW70%
70
69
1
150 |
CW70%
70
69
150 |
CW70%
115
230 |
CW70%
84
8 |
Extra Hard
UTS
YS
EL
HV |
|
|
|
|
Spring
UTS
YS
EL
HV |
|
|
|
|
Ex. Spring
UTS
YS
EL
HV |
|
|
|
|
|
|
|
|
|
CHART FOOTNOTES
1 Lbs. per cubic inch @ 68°F (annealed)
2 Elastic modulus in tension x 106 P.S.I.
3.% IACS at
68°F (annealed)
4. BTU per foot per hour per °F at 68°F (annealed)
5. Inches ber inch x 10-6 from 68°F to 572°F
6. Reference specification for strip
7. Ultimate tensile strength x 1000 P.S.I.
8. 0.2% offset yield strength x 1000 P.S.I. Yield strengths are not used or accepted as specifications by brass mills; but because of their usefulness, values are given here for design purpose.
9. % elongation in 2". Elongation values vary considerably with thickness. The rolled temper data given are base on thicknesses ranging from .010" to .035" strip.
10. Approximate Vickers hardness - HV unless otherwise specified.
11. Standard heat treatment 2 hrs. at 600°F (3 hrs. @ 600°F for annealed temper)
12. Standard heat treatment 2 hrs. at 700°F (2 hrs. @ 675°F for TS04)
|
|
|
|
|
|