Reroll Capabilities and Alloys / Steels


Alloys available are: S30100,
S30200, S30400, S30403
(304L), S31600, S31603 (316L),
S43000, N06600 (Inconel).

Tempers up to Full Hard (200
KSI Max)

Gauges from .0025" - .040" x
3.000" Max width

Minimum buy is generally
100 lbs.




If you are looking for
something outside
the parameters listed,
please give us a call!

We may have a solution!

S30100

301

Fe 17Cr 7Ni		 S30200

302

Fe 18Cr 9Ni		 S30403

304L

Fe 19Cr 10Ni		 S30500

305

Fe 18Cr 12Ni		 S31008*

310 S

Fe 25Cr 20Ni		 S31600

316

Fe 17Cr 12Ni
2.5Mo		 S32100

321

Fe 18Cr 10Ni
.4Ti		 S40900

409

Fe 11Cr 		S43000

430

Fe 16Cr		 G100800

1008

Fe .08C		 K00100

Iron

Fe .005C
Density (1)
Modulus (2)
Elect.Cond.(3)
Therm.Cond.(4)
Therm. Exp.(5)
ASTM(6)		 .285
28
2.5
9.4
9.5
A666		 .285
28
2.5
9.4
9.5
A666		 .284
28
2.4
9.4
9.9
A666		 .29
28
2.4
9.4
9.9
A240		 .29
28
2.4
9.4
9.9
A240		 .29
28
2.2
8.2
9.0
A666		 .29
28
2.3
9.4
9.0
A240		 .28
29
2.8
14.4
6.1
A240		 .28
29
2.8
13.8
6.1
A176		 .283
29


6.7
A109		 .278

16
Annealed
UTS7
YS8
EL9
HV10
110 Nom.
40 Nom.
60 Nom.
170 Nom.
90 Nom.
40 Nom.
50 Nom.
170 Nom.
84 Nom.
42 Nom.
55 Nom. 170 Nom.
85 Nom.
38 Nom.
55 Nom.
170 Nom.
95 Nom.
45 Nom.
45 Nom.
170 Nom.
84 Nom.
42 Nom.
50 Nom. 150 Nom.
90 Nom.
35 Nom.
45 Nom.
150 Nom.
55-68
25-41
20-38
123
65-80
40-60
18-30
144-176
skin rolled
40-55
25-40
24 Min.
125 Max.

40-60
30-45
25 Num.
115 Num.
1/4 Hard
UTS
YS
EL
HV
125 Min
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
125 Min.
75 Min.
25 Min.
250 Nom.
58
25
25
78-90
60-78
3-19
172-205

45-65
--
13-27
107-137
1/2 Hard
UTS
YS
EL
HV
150 Min
110 Min
15 Min.
300 Nom.
140 Min.
110 Min.
15 Min.
300 Nom.
140 Min.
110 Min.
15 Min.
300 Nom.
130 Min.
110 Min.
10 Min.
300 Nom.
130 Min
110 Min
15 Min.
300 Nom.
130 Min
110 Min
10 Min.
300 Nom.
130 Min.
110 Min.
8 Min.
300 Nom.
75
74
16
172
90-100
76-92
3-7
205-228
55-75
--
4-16
125-170
3/4 Hard
UTS
YS
EL
HV
175 Min
135 Min
10 Min.
350 Nom.
165 Min.
135 Min.
10 Min.
350 Nom.
160 Min.
135 Min.
5 Min.
350 Nom.
150 Min.
135 Min.
5 Min.
350 Nom.
150 Min.
135 Min.
10 Min.
350 Nom.
150 Min
135 Min
10 Min.
350 Nom.
150 Min.
135 Min.
5 Min.
350 Nom.
82
81
9.5
190
98-110
90-103
1-7
222-242

Hard
UTS
YS
EL
HV
185 Min
140 Min
8 Min
390 Nom.
175 Min
140 Min
8 Min
390 Nom.
170 Min. 140 Min.
2 Min.
390 Nom.


170 Min.
140 Min.
2 Min.
390 Nom.

101
102
3
222
107-115
100-110
1-2
228-246
80-100
--
--
185 Min.
75-85
65-80

150 Num.

maximum strength and work hardening standard general purpose stable properties low C stable properties low C low work hardening good formability high temp oxidation resistance good formability maximum corrosion resistance excellent resistance to oxidation & corrosion ferretic economical use for corrosion & oxidation resistance ferretic general use for corrosion & oxidation resistance
better formability
Magnetic No No No No No No No Yes Yes Yes Yes



*Dependent upon material availability
CHART FOOTNOTES
1 Lbs. per cubic inch @ 68°F (annealed)
2 Elastic modulus in tension x 106 P.S.I.
3.% IACS at 68°F (annealed)
4. BTU per foot per hour per °F at 68°F (annealed)
5. Inches ber inch x 10-6 from 68°F to 572°F
6. Reference specification for strip
7. Ultimate tensile strength x 1000 P.S.I.
8. 0.2% offset yield strength x 1000 P.S.I. Yield strengths are not used or accepted as specifications by brass mills; but because of their usefulness, values are given here for design purpose.
9. % elongation in 2". Elongation values vary considerably with thickness. The rolled temper data given are base on thicknesses ranging from .010" to .035" strip.
10. Approximate Vickers hardness - HV unless otherwise specified.
11. Standard heat treatment 2 hrs. at 600°F (3 hrs. @ 600°F for annealed temper)
12. Standard heat treatment 2 hrs. at 700°F (2 hrs. @ 675°F for TS04)